改良9Cr鋼のクリープ損傷過程における結晶粒内ひずみ分布のEBSDによる評価
藤山 一成小川 明寛原田 和真來海 博央
著者情報
ジャーナル フリー

2015 年 64 巻 2 号 p. 94-99

詳細
抄録

Creep damage evaluation by EBSD(Electron BackScatter Diffraction pattern) method was conducted on the ferritic heat resistant Mod.9Cr steel as the turbine piping material. Creep damage was imposed under the condition of 600℃/130MPa and 650℃/100MPa with various interruption hours. The longitudinal mid-section of specimen was cut and observed by EBSD equipment and then Boundary maps, IPF(Inverse Pole Figure) maps, KAM(Kernel Average Misorientation) maps and GROD(Grain Reference Orientation Deviation) maps were obtained. Boundary maps showed the decreasing sub-boundary length having relatively small rotation angles with the increasing time fraction or the accumulated macroscopic creep strain. The misorientation parameters obtained from KAM maps and GROD maps showed decreasing trend with increasing time fraction. The distribution function of GROD was regressed on the basis of continuously distributed dislocation theory and its representative coefficient parameter AG showed good correlation with time fraction or accumulated creep strain. AG multiplied by equivalent grain diameter ld seemed to show slightly higher sensitivity to creep strains. A good correlation between the void length and the creep strain evaluated from AGld was observed. The AGld parameter was considered as an effective quantity obtained from EBSD observation to evaluate creep strain intensity at the grains with and without creep voids irrespectively.

著者関連情報
© 2015 日本材料学会
前の記事 次の記事
feedback
Top